Product Details:
Payment & Shipping Terms:
|
| Material: | Steel | Heat Treatment: | N+T Q+T |
|---|---|---|---|
| Max Power: | 5MW | Melting Process: | EF+LF+VD |
| Size: | As Drawing | Application: | Machinery Parts |
| High Light: | turbine rotor forging,steam turbine shaft |
||
Large Steam Turbine Rotor Forging Wind Power Generation Turbine Main Shaft
Products:
wind power generation main shaft,GE draught fan,wind power turbine shaft, 34CrNiMo6 main shaft,coupling,wind power generation forging
Products reference:
| Material | 34CrNiMo6,18CrNiMo7-6,4140 |
| Max power | 5MW |
| Application |
In main engine box of wind power generation,blades rotate main shaft by wind energy,connect to accelerator |
| Melting process | EF+LF+VD |
| Production process |
Forging+heat treatment+rough machining+finish machining |
| Forging ratio |
≥3.5 |
| Applicable standard | ASTM,ASME,DIN,JIS,ISO,BS,API,EN |
| Executive standard | JB/GB/EN/DIN/JIS/ASME/ASTM/ISO |
| Certification authority | ISO,BV,SGS, IST, UL,CTI |
| Delivery term |
Rough machining(N+T);finish machining(Q+T) |
|
Test equipment |
Spectrograph,UT device,tensile and compact test machine,metalloscope,outside micrometer,bore dial indicator,hardness test machine |
| Service | Our service included the forging, process, heat treatment, finish machining, package, local logistics, customers clearance and maritime transport. We took the customer’s requirements as the principal thing, and pay attention on the products quality. |
3, Custom properties
| Material elements | C | Si | Mn | P | S | Cr | Ni | Mo |
Others |
| 34CrNiMo6 | 0.30-0.38 | ≤0.040 | 0.50-0.80 | ≤0.035 | ≤0.035 | 1.30-1.70 | 1.30-1.70 | 0.15-0.30 | |
| 4140 | 0.38-0.43 | 0.15-0.35 | 0.60-0.90 | ≤0.035 | ≤0.040 | 0.80-1.10 | -- | 0.15-0.25 | - |
| 18CrNiMo7-6 | 0.15-0.21 | 0.17-0.35 | 0.50-0.90 | ≤0.025 | ≤0.025 | 1.50-1.80 | 1.40-1.70 | 0.25-0.35 |
| Mechanical property |
Dia.(mm) |
TS/Rm(Mpa) |
YS/Rp0.2(Mpa) |
EL/A5(%) |
RA/Z(%) |
Type Of notch |
Impact energy |
HBW |
| 34CrNiMo6 | Ø15 | 750-900 | 450-600 | ≥13 | ≥55 | V | -40℃≥20 | ≤269HBS |
| 4140 | Ø10 | 740~1000 | 450~850 | ≥12 | ≥25 | V | ≥40 | ≤250HBS |
| 18CrNiMo7-6 | Ø15 | ≥980 | ≥785 | ≥9 | ≥40 | V | ≥47 | ≤269HBS |
Process procedure:
Forging process flow quality control: Raw material steel ingot into warehouse(test the chemical content) → Cutting→ Heating(Furnace temperture test) → Heat treatment after forging(Furnace temperture test) Discharge the furnace(blank inspection)→ Machining→ Inspection(UT,MT,Visal diamention, hardness)→ QT→ Inspection(UT, mechanical properties, hardness, grain size)→ Finish machining→ Inspection (dimension)→ Packing and Marking(steel stamp, mark)→ Storage Shipment
Commerce clause
| Max weight | 35T |
| MOQ | 1PC |
| Delivery time | 30-50 days |
| Package | Plywood case,wood pallet,steel frame |
| Delivery term | FOB;CIF;CFR；DDU； |
| Payment terms | T/T,LC |
| Type of shipping |
By ocean,air |
Keywords:
Large middle small type wind power main shaft forging, 0.8MW;1.2MW;2MW;3.MW;3.6MW;5MW various large middle small draught fan shaft
Contact Person: Mr. Arnold
Tel: +86-15-15-15-81-878
Fax: 86-512-58360318
| Sales office:A 509,HuaJian Mansion,Zhangjiagang City,JiangSu Province,China | |
| +86--13914905080 | |
| arnoldxue@163.com | |